It is mainly used for the partition walls of the carbonization chamber and combustion chamber of coke ovens, the regenerators and slag chambers of steel-making open-hearth furnaces, soaking furnaces, refractory materials of glass melting furnaces and ceramic firing kilns, and other kiln vaults. Load-bearing parts. It is also used in high-temperature load-bearing parts of hot blast furnaces and acidic open-hearth furnace tops.
Payment :
In AdvanceProduct Origin :
ChinaShipping Port :
Shanghai PortLead Time :
15 Working days| Item | Clay-bound SiC | Clay-bound SiC | Mullite bonded SiC | SiO2-bound SiC | SiO2 combined with SiC | |
| 1 | 2 | |||||
| Bulk density /g - cm-3 | 2.4-2.6 | Approximate 2.5 | - | 2.70-2.75 | 2.66 | 2.78 |
| Porosity, % | 15-25 | 14～18 | 14～16 | 45115 | 13.3 | 5.8 |
| Normal temperature compressive strength/MPa | - | Approximate 100 | ＞130 | 120 | 150 | |
| Coefficient of linear expansion, ℃-1(20 to 1000 ℃) | - | 4.6×10 -6 | - | ＜4.9×10 -6 | 4.8×10 -6 | 4.8×10 -6 |
| Thermal conductivity, W - ( m - k ) -1(1000 ℃) | - | 11 | - | 15.7-16.9 | 15.7（ 1200 ℃） | 16.2（1200 ℃） |
| ω(SiC), % | 50～90 | ＞85 | ＞70 | ≥90 | 88 | 89.8 |
| ω(SiO2), % | - | - | - | - | 9.5 | 8.9 |
| ω(Al2O3), % | - | - | - | - | 1.5 |
0.5 |
| ω(Fe2O3), % | - | - | - | - | 0.7 | 0.3 |
Applications of bricks:
is mainly used for the partition walls of the carbonization chamber and combustion chamber of coke ovens, the regenerators and slag chambers of steel-making open-hearth furnaces, soaking furnaces, refractory materials of glass melting furnaces and ceramic firing kilns, and other kiln vaults. Load-bearing parts. It is also used in high-temperature load-bearing parts of hot blast furnaces and acidic open-hearth furnace tops.
Tags :
Tel : +86 1850 168 9323
Email : [email protected]
Skype : +86 199 9192 1006
Whatsapp : +86 185 0168 9323
Address : Room D50, 5th Floor, Building B, Building 18, No. 505, Xinbei Road, Minhang District, Shanghai
© 2024 Shanghai Du Yusen Industrial Co., Ltd All Rights Reserved.
EN
HI